Name: λ/4-Quarzglasfenster, 10 mm Durchm., 1 mm Dicke, NIR-I-beschichtet
Brand: TECHSPEC
SKU: 18-334
Price: €112,50

λ/4-Quarzglasfenster, 10 mm Durchm., 1 mm Dicke, NIR-I-beschichtet

TECHSPEC® λ/4 UV Fused Silica Windows

Produkt #18-334 3-4 Tage

- +

€112,50

Stk. 1-5
€112,50

Stk. 6+
€90,00

Mengenrabatte
Angebotsanfrage

+ Merkliste
Erstellen Sie einen Account oder melden Sie sich an, um auf gespeicherte Listen zuzugreifen.

Vergleichen

Downloadbereich

Abbe-Zahl (v_d):

67.8

Fase:

Protective as needed

Freie Apertur (%):

Freie Apertur CA (mm):

9.00

Durchmesser (mm):

10.00 +0.00/-0.10

Dicke (mm):

1.00 ±0.10

Beschichtung:

NIR I (600-1050nm)

Beschichtungsspezifikation:

R_avg ≤0.5% @ 600 - 1050nm

Thermischer Ausdehnungskoeffizient CTE (10^-6/°C):

0.52 (+5 to +35°C)
0.57 (0 to +200°C)
0.48 (-100 to +200°C)

Dichte (g/cm³):

2.20

Kanten:

Fine Ground

Brechungsindex n_d:

1.458

Knoop-Härte (kg/mm²):

522

Parallelität (Bogenminuten):

Poisson-Zahl:

0.16

Substrat: Many glass manufacturers offer the same material characteristics under different trade names. Learn More

Fused Silica (Corning 7980)

Oberflächenqualität:

40-20

Transmittierte Wellenfront, P-V:

λ/4

Typ:

Protective Window

Wellenlängenbereich (nm):

600 - 1050

Elastizitätsmodul (GPa):

7 J/cm² @ 1064nm, 10ns

Konformität mit Standards

RoHS 2015:

Konform

Konformitätszertifikat:

Anzeigen

Reach 235:

Konform

Beschreibung Produktfamilie

Verfügbar unbeschichtet sowie BBAR-beschichtet für UV, VIS und NIR
Ideal für Bildverarbeitungsanwendungen
Standarddurchmesser von 5 bis 200 mm
1λ- oder λ/10-Fenster aus UV-Quarzglas sind ebenfalls verfügbar

TECHSPEC^® λ/4-Fenster aus UV-Quarzglas haben eine Oberflächenqualität von 40-20 und einen transmittierten Wellenfrontfehler von λ/4. Dies macht sie ideal für Bildverarbeitungsanwendungen. Die Fenster bestehen aus UV-Quarzglassubstraten und bieten eine hohe Transmission vom ultravioletten über den sichtbaren bis zum nahinfraroten Bereich. Es sind breitbandige Antireflexionsbeschichtungen (BBAR) verfügbar, um Reflexionsverluste zu minimieren und die Transmission zu erhöhen. TECHSPEC^® λ/4-Fenster aus UV-Quarzglas werden in optischen Bildgebungsanwendungen, in Laseranwendungen mit geringer oder mittlerer Leistung und als Schutzfenster für Anwendungen, die eine hohe UV-Transmission erfordern, eingesetzt.

Technische Informationen

FUSED SILICA
	Typical transmission of a 3mm thick, uncoated fused silica window across the UV - NIR spectra. Click Here to Download Data
	Typical transmission of a 3mm thick fused silica window with MgF2 (400-700nm) coating at 0° AOI. The blue shaded region indicates the coating design wavelengh range, with the following specification: R_avg ≤ 1.75% @ 400 - 700nm (N-BK7) Data outside this range is not guaranteed and is for reference only. Click Here to Download Data
	Typical transmission of a 3mm thick fused silica window with UV-AR (250-425nm) coating at 0° AOI. The blue shaded region indicates the coating design wavelengh range, with the following specification: R_abs ≤ 1.0% @ 250 - 425nm R_avg ≤ 0.75% @ 250 - 425nm R_avg ≤ 0.5% @ 370 - 420nm Data outside this range is not guaranteed and is for reference only. Click Here to Download Data
	Typical transmission of a 3mm thick fused silica window with UV-VIS (250-700nm) coating at 0° AOI. The blue shaded region indicates the coating design wavelengh range, with the following specification: R_abs ≤ 1.0% @ 350 - 450nm R_avg ≤ 1.5% @ 250 - 700nm Data outside this range is not guaranteed and is for reference only. Click Here to Download Data
	Typical transmission of a 3mm thick fused silica window with VIS-EXT (350-700nm) coating at 0° AOI. The blue shaded region indicates the coating design wavelengh range, with the following specification: R_avg≤ 0.5% @ 350 - 700nm Data outside this range is not guaranteed and is for reference only. Click Here to Download Data
	Typical transmission of a 3mm thick fused silica window with VIS-NIR (400-1000nm) coating at 0° AOI. The blue shaded region indicates the coating design wavelengh range, with the following specification: R_abs≤ 0.25% @ 880nm R_avg≤ 1.25% @ 400 - 870nm R_avg≤ 1.25% @ 890 - 1000nm Data outside this range is not guaranteed and is for reference only. Click Here to Download Data
	Typical transmission of a 3mm thick fused silica window with VIS 0° (425-675nm) coating at 0° AOI. The blue shaded region indicates the coating design wavelengh range, with the following specification: R_avg≤ 0.4% @ 425 - 675nm Data outside this range is not guaranteed and is for reference only. Click Here to Download Data
	Typical transmission of a 3mm thick fused silica window with YAG-BBAR (500-1100nm) coating at 0° AOI. The blue shaded region indicates the coating design wavelengh range, with the following specification: R_abs ≤ 0.25% @ 532nm R_abs ≤ 0.25% @ 1064nm R_avg≤ 1.0% @ 500 - 1100nm Data outside this range is not guaranteed and is for reference only. Click Here to Download Data
	Typical transmission of a 3mm thick fused silica window with NIR I (600 - 1050nm) coating at 0° AOI. The blue shaded region indicates the coating design wavelengh range, with the following specification: R_avg≤ 0.5% @ 600 - 1050nm Data outside this range is not guaranteed and is for reference only. Click Here to Download Data
	Typical transmission of a 3mm thick fused silica window with NIR II (750 - 1550nm) coating at 0° AOI. The blue shaded region indicates the coating design wavelengh range, with the following specification: R_abs ≤ 1.5% @ 750 - 800nm R_abs ≤ 1.0% @ 800 - 1550nm R_avg≤ 0.7% @ 750 - 1550nm Data outside this range is not guaranteed and is for reference only. Click Here to Download Data